不破碎锻造钢球
Spec.
|
C
|
Si
|
Mn
|
S
|
P | Cr | Ni | Cu |
20-150mm | 0.5-0.9 | 0.17-0.37 | 0.7-1.2 | < 0.035 | < 0.035 | <1 | < 0.25 | < 0.25 |
钢球直径 (MM) |
A型材质 | B型材质 | C型材质 | D型材质 | ||||||||
表面硬度 | 内心硬度 | 冲击值 | 表面硬度 | 内心硬度 | 冲击值 | 表面硬度 | 内心硬度 | 冲击值 | 表面硬度 | 内心硬度 | 冲击值 | |
φ25 | 60-65 | 58-63 | ≥12J/CM2 | |||||||||
φ30 | 60-65 | 55-60 | ≥12J/CM2 | |||||||||
φ35 | 60-65 | 55-60 | ≥12J/CM2 | |||||||||
φ40 | 60-65 | 55-63 | ≥12J/CM2 | 60-65 | 60-65 | ≥12J/CM2 | ||||||
φ50 | 60-65 | 45-50 | ≥12J/CM2 | 60-65 | 60-65 | ≥12J/CM2 | ||||||
φ60 | 60-65 | 42-47 | ≥12J/CM2 | 60-65 | 60-65 | ≥12J/CM2 | ||||||
φ70 | 60-65 | 40-45 | ≥12J/CM2 | 60-65 | 60-65 | ≥12J/CM2 | ||||||
φ75 | 60-65 | 40-45 | ≥12J/CM2 | 60-65 | 60-65 | ≥12J/CM2 | ||||||
φ80 | 60-65 | 37-42 | ≥12J/CM2 | 60-65 | 60-65 | ≥12J/CM2 | ||||||
φ90 | 60-65 | 37-42 | ≥12J/CM2 | 58-63 | 52-60 | ≥12J/CM2 | ||||||
φ100 | 58-63 | 37-42 | ≥12J/CM2 | 53-58 | 42-58 | ≥12J/CM2 | 58-62 | 58-60 | ≥14J/CM2 | 60-65 | 60-65 | ≥14J/CM2 |
φ110 | 55-63 | 35-40 | ≥12J/CM2 | 53-58 | 45-50 | ≥12J/CM2 | 58-62 | 58-60 | ≥14J/CM2 | 60-65 | 60-65 | ≥14J/CM2 |
φ120 | 55-63 | 35-40 | ≥12J/CM2 | 53-58 | 45-50 | ≥12J/CM2 | 55-62 | 58-60 | ≥14J/CM2 | 60-65 | 60-65 | ≥14J/CM2 |
φ125 | 50-55 | 35-40 | ≥12J/CM2 | 53-58 | 45-50 | ≥12J/CM2 | 55-62 | 52-58 | ≥14J/CM2 | 60-65 | 58-63 | ≥14J/CM2 |
φ130 | 50-55 | 35-40 | ≥12J/CM2 | 53-58 | 40-45 | ≥12J/CM2 | 55-58 | 50-55 | ≥14J/CM2 | 60-65 | 58-63 | ≥14J/CM2 |
φ140 | ≥12J/CM2 | 53-58 | 40-45 | ≥12J/CM2 | 55-58 | 45-55 | ≥14J/CM2 | 60-65 | 55-60 | ≥14J/CM2 | ||
φ150 | ≥12J/CM2 | 53-58 | 40-45 | ≥12J/CM2 | 55-58 | 40-45 | ≥14J/CM2 | 60-65 | 53-58 | ≥14J/CM2 |
公称直径 NOMINAL DIAMETER(mm)(INS) |
直径允许偏差 DIAMETRICAL TOLERANCE(mm) |
每个钢球平均重量 APPOX AVERAGE WEIGHT PER BALL |
每吨钢球平均个数 AVERAGE NUMBER OF BALLS PER MT |
20 4/5 25 1 30 11/4 40 11/2 |
+2 -1 |
32 64 116 263 |
31250 15625 8620 3802 |
50 2 60 21/2 70 23/4 80 31/4 |
+3 -1 |
513 888 1490 2104 |
1949 1126 671 475 |
90 33/4 100 4 110 41/2 120 5 130 51/4 140 51/2 150 6 |
+4 -2 |
2996 4110 5070 7102 9030 11278 13872 |
334 243 183 141 111 89 72 |
山东东铁铸锻有限公司
电 话:0531-83207968\83318289
侯经理:18954519298\15764168666
传 真:0531-83318289
邮 箱:sales@grindingballs.net.cn
地 址:山东省济南市章丘普集凤凰工业园
在线留言
Copyright © 山东东铁铸锻有限公司 版权所有 鲁ICP备14013354号 网站建设:中企动力 济南